ARCRETE PRODUCT DATA SHEET
Data
Sheet |
Product Application
GENERIC TYPE: AMINE CURED
100% SOLIDS EPOXY PRIMER/REBUILD
DESCRIPTION AND RECOMMENDED USES: ARCOR™ ARCRETE is a
solvent free epoxy “concrete” designed for use in repair of
concrete in areas exposed to aggressive chemicals. ARCRETE
produces a tough, chemical resistant coating which reaches full
cure within 72 hours, unlike regular concrete, which allows for
rapid turnaround of the process environment. ARCRETE can be
top-coated with any ARCOR™ or ARCOR™ coating to provide for
protection in the most aggressive acid or caustic environments.
Low viscosity makes ARCRETE suitable as a primer when unfilled.
FOR INDUSTRIAL USE ONLY
SPECIFICATION DATA
|
TEMPERATURE: Immersion
service
Max. 100ºF (38ºC); Spike to 120ºF (49ºC)3 Hrs
Dry to 120ºF (49ºC); spike to 140ºF (60ºC) 3 Hrs
CHEMICAL RESISTANCE:
Water: Excellent
Alkalines: Good
Inorganic Acids: Good
Organic Acids: Fair
Organic Solvents: Fair
ABRASION: Very Good
FLEXIBILITY: Fair
Very Good with Fiberglass Mat; 1.5 oz/ft2 (.5 KG/M2)
FILM THICKNESS: 10 mils unfilled, as needed filled
APPLICATIONS: Secondary containment, Industrial flooring,
Concrete tank supports, Chemical drain troughs, Sump Basins,
Rebuilding of concrete in any aggressive chemical area.
SOLIDS BY VOLUME: 100%
VISCOSITY: 700-900 cps unfilled
POT LIFE: 30 MIN/GAL @ 75ºF
MIX RATIO: 2:1 by Volume (Base:Activator)
100 gm: 44.9 gm by Weight
COLOR: Clear Amber
SHELF LIFE: 5 Years at 55-95ºF (13-35ºC)
COVERAGE: 160 ft2(14.8 M2)/gal/coat @ 10 mils
WEIGHT PER GALLON: 9.0 lbs (4.1 KG)
1 KG=56 cu. in.
ORDER INFORMATION: To place orders
and/or obtain pricing information contact:
ARCOR Epoxy Inc. PO Box 273
South Dennis, MA 02660
TEL: 800-878-9593; FAX: 888-878-9593 |
Manufacturer makes no warranty
either expressed or implied including warranties of
merchantability or fitness for a particular purpose for this
product. Under no circumstances will the manufacturer be liable
for incidental, consequential or other damages, breach of
warranty, strict liability, or any other theory arising out of use
of this product.
|