EE-101 PRODUCT DATA SHEET
Data
Sheet | Product Application
GENERIC TYPE:
AMINE
CURED 100% SOLIDS EPOXY 3.6 NOVOLAC PRIMER, TOPCOAT
DESCRIPTION AND RECOMMENDED USES:
ARCOR®
EE-101 is a solvent free, Ultra 3.6 functionality epoxy Novolac
coating. It's designed for use in the most aggressive chemical and
high temperature environments typically thought beyond the
abilities of epoxies. ARCOR® EE-101 can be used on ferrous and
non-ferrous metals and concrete. Excellent for Nitric,
Hydrochloric, Glacial Acetic Acid and Methanol. As the lowest
viscosity epoxy 3.6 functionality Novolac available
ARCOR®
EE-101 is suitable as a primer as well as a topcoat. The absence
of fillers and pigments make it the highest performing Novolac
coating commercially available.
FOR INDUSTRIAL USE ONLY
SPECIFICATION DATA
TEMPERATURE:
Immersion service
Max.350F(177ºC); Spike to 450ºF(3 Hrs)
Recommended force cure at 250ºF@ 2 hrs.CHEMICAL
RESISTANCE:
Water: Excellent
Alkalines: Excellent
Inorganic Acids: Excellent
Organic Acids: Excellent
Organic Solvents: Excellent
ABRASION: Good
FLEXIBILITY: Good
FILM THICKNESS:
8-10 mils (.26 mm)/coat Exterior: 2 coats, Immersion: 2-3 coats
APPLICATIONS:
Aggressive Chemical Tank Linings and Secondary Containment Areas.
Excellent when Force Cure is not available.
SOLIDS BY
VOLUME:
100%
VISCOSITY: 9,000-15,000 cps
POT LIFE: 15 MIN @ 72ºF
MIX RATIO: 4:1 by Volume (Base:Activator) 100gm: 23.1 gm by
Weight
COLOR: Clear Amber (not pigmented)
SHELF LIFE: 5 Years at 55-95ºF (13-35ºC)
COVERAGE: 160ft²(15M²)/gal/coat(theoretical)
WEIGHT PER GALLON: 9.3 lbs (4.2 KG)
ORDER INFORMATION: To place orders
and/or obtain pricing information contact:
ARCOR Epoxy Inc. PO Box 273
South Dennis, MA 02660
TEL: 800-878-9593; FAX: 888-878-9593
|
Manufacturer makes no warranty
either expressed or implied including warranties of
merchantability or fitness for a particular purpose for this
product. Under no circumstances will the manufacturer be liable
for incidental, consequential or other damages, breach of
warranty, strict liability, or any other theory arising out of use
of this product.
|