EE-15 PRODUCT DATA SHEET
Data
Sheet | Product Application
GENERIC TYPE: AMINE CURED
100% SOLIDS EPOXY PRIMER, TOPCOAT
DESCRIPTION AND RECOMMENDED USES: ARCOR™ EE-15 is a solvent free, ceramic filled high functionality
epoxy Novolac coating suitable for immersion and non immersion service, particularly in aggressive and alkali environments with elevated temperatures. ARCOR™ EE-15 produces a tough, chemical resistant coating on ferrous metals and concrete.
As a low viscosity epoxy Novolac ARCOR™ EE-15 is suitable for hand or spray application on metals or concrete. The long pot-life and over coat window make this ideal for larger surface areas.
FOR INDUSTRIAL USE ONLY
SPECIFICATION DATA
|
TEMPERATURE: Immersion
service
Max.365F(130ºC); Spike to 400ºF (3 Hrs)
CHEMICAL RESISTANCE:
Water: Excellent
Alkalines: Excellent
Inorganic Acids: Excellent
Organic Acids: Excellent
Organic Solvents: Excellent
ABRASION: Very Good
FLEXIBILITY: Good
Very good with Fiberglass Mat; 1.5 oz/ft² (.5 KG/M²)
FILM THICKNESS:
10 -20 mils(.25-.50 mm)/coat
Splash: 2 coats, Immersion: 2-3 coats
APPLICATIONS: Aggressive Chemical Tank Linings, Acids,
Caustics, Alchohols, Denim. Excellent for Secondary Containment's.
Excellent when force cure is not available.
SOLIDS BY VOLUME: 100%
VISCOSITY:
25,000-40,000 cps
POT LIFE: 25 MIN/KG @ 72ºF
MIX RATIO:
2:1 by Volume (Base:Activator) 100 gm:
40 gm by weight
COLOR:
Gray, Light Gray, Red
SHELF LIFE: 5 Years at 55-95ºF (13-35ºC)
COVERAGE:
80-160 ft2(7.5-15 M2)/ gal / coat
WEIGHT PER GALLON:
13.6 lbs (6.2 KG, 231 cu.in.)
1-KG Kit @ 37.5 cu.in .
ORDER INFORMATION: To place orders
and/or obtain pricing information contact:
ARCOR Epoxy Inc. PO Box 273
South Dennis, MA 02660
TEL: 800-878-9593; FAX: 888-878-9593
|
Manufacturer makes no warranty
either expressed or implied including warranties of
merchantability or fitness for a particular purpose for this
product. Under no circumstances will the manufacturer be liable
for incidental, consequential or other damages, breach of
warranty, strict liability, or any other theory arising out of use
of this product.
|