EE-99K-C PRODUCT DATA SHEET
Data
Sheet | Product Application
GENERIC TYPE:
AMINE CURED 100% SOLIDS EPOXY QUICK-SET REBUILDING COMPOUND
DESCRIPTION AND RECOMMENDED
USES: ARCOR® EE-99K-C is a solvent
free fast cure rebuilding epoxy for high abrasion areas.
EE-99K-C sets in 6 minutes and can get put in service within 1
hour regardless of temperature. EE-99K-C is filled with ceramic
beads and Kevlar fiber giving excellent abrasion and impact
restance. EE-99K-C has good resistance in a wide variety of
chemical environments and has heat resistance to 450ºF. EE-99K-C
has an easy to use 1:1 mix ratio and can be applied overhead or
vertically.
FOR INDUSTRIAL USE ONLY
SPECIFICATION DATA
|
TEMPERATURE: Immersion service Max. 225ºF
(93ºC) ; Dry to 450ºF (218ºC).
CHEMICAL RESISTANCE:
Water: Excellent
Alkalies: Very Good
Inorganic Acids: Very Good
Organic Acids: Fair
Organic Solvents: Good
ABRASION: Excellent
FLEXIBILITY: Fair
BOND STRENGTH: 1,200 psi @ 1/2 hour;
2,200 psi @ 1 hour; 3,200 psi @ 24 hr.
HARDNESS, SHORE D: 25 @ 10 min.; 60 @ 20
min.;
82 @ 1hr.; 97 @ 24 hr.
APPLICATIONS: Repair burst pipes, tanks,
pumps and the like which contain liquids or gases. Use for
bonding Dissimilar Metals. Use for Concrete, Metal, Glass, Wood.
FILM THICKNESS: up to 1000 mils/coat
SOLIDS BY VOLUME: 100%
VISCOSITY: Putty
POT LIFE: 6 MIN / KG @ 72ºF
DENSITY: 1.81
MIX RATIO: 1:1 by
Volume (Base:Activator)
100 gm: 100 gm by Weight
COLOR: Gray
SHELF LIFE: 5 Years at 55-95ºF (13-35ºC)
COVERAGE: varies with thickness applied
WEIGHT PER GALLON: 15.1 lbs (6.9 KG, 231
cu.in.)
1-KG Kit (34 Cu.In);
ORDER INFORMATION: To place orders
and/or obtain pricing information contact:
ARCOR Epoxy Inc. PO Box 273
South Dennis, MA 02660
TEL: 800-878-9593; FAX: 888-878-9593 |
Manufacturer makes no warranty
either expressed or implied including warranties of
merchantability or fitness for a particular purpose for this
product. Under no circumstances will the manufacturer be liable
for incidental, consequential or other damages, breach of
warranty, strict liability, or any other theory arising out of use
of this product.
|