GENERIC TYPE:   AMINE CURED 100% SOLIDS EPOXY PRIMER/REBUILD

DESCRIPTION AND RECOMMENDED USES:  ARCOR™ ARCRETE is a solvent free epoxy “concrete” designed for use in repair of concrete in areas exposed to aggressive chemicals. ARCRETE produces a tough, chemical resistant coating which reaches full cure within 72 hours, unlike regular concrete, which allows for rapid turnaround of the process environment. ARCERTE can be top-coated with any ARCOR™ or ARCOR™ coating to provide for protection in the most aggressive acid or caustic environments. Low viscosity makes ARCRETE suit- able as a primer when unfilled.

FOR INDUSTRIAL USE ONLY

SPECIFICATION DATA:

TEMPERATURE: Immersion service

Max. 100ºF (38ºC); Spike to 120ºF (49ºC)3 Hrs Dry to 120ºF (49ºC); spike to 140ºF (60ºC) 3 Hrs

 

CHEMICAL RESISTANCE:

Water:                               Excellent

Alkalies:                            Good

Inorganic Acids:             Good

Organic Acids:                Fair

Organic Solvents:          Fair

 

SOLIDS BY VOLUME: 100%

VISCOSITY: 700-900 cps unfilled

POT LIFE: 30 MIN/GAL @ 75ºF

MIX RATIO: 3.2 by Volume (Base:Activator) 100 gm: 62 gm by Weight

COLOR:  Clear Amber

ABRASION:  Very Good

FLEXIBILITY: Fair Very Good with Fiberglass Mat; 1.5 oz/ft2 (.5 KG/M2)

FILM THICKNESS: 10 mils unfilled, as needed filled

APPLICATIONS: Secondary containment, Industrial flooring, Concrete tank supports, Chemical drain troughs, Sump Basins, Rebuilding of concrete in any aggressive chemical area.

SHELF LIFE:  5 Years at 55-95ºF (13-35ºC)

COVERAGE: 160 ft2(14.8 M2)/gal/coat @ 10 mils

WEIGHT PER GALLON: 9.3 lbs (4.21 KG)

 

ORDER INFORMATION:

To place orders and/or obtain pricing information contact:

ARCOR Epoxy Inc. PO Box 273

South Dennis, MA 02660

TEL: 800-878-9593; FAX: 888-878-9593

Contact Us!

Manufacturer makes no warranty either expressed or implied including warranties of merchant ability or fitness for a particular purpose for this product. Under no circumstances will the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability, or any other theory arising out of use of this product.

APPLICATION SHEET

REVISED 5/2013

SEE MATERIAL SAFETY DATA SHEET BEFORE HANDLING THIS PRODUCT

 

SURFACE PREPARATION:

Metal surfaces are to be cleaned and degreased then abraisive blasted with chloride free abrasive. Exterior applications to SSPC-SP-10 near white metal finish minimum 3 mil profile. Immersion applications to SSPC SP-5 white metal, 3 to 5 mil profile.Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted surfaces to be rebuilt as quickley as pos- sible to prevent oxidation of surface. Prime surface with ARCOR™ARCRETE (unfilled) or ARCOR™ EE-31 or EE-031.1

Concrete surfaces should be degreased. Degreased surface shall be high pressure washed, acid etched and high pres- sure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abra- sive blasted to clean concrete.

MIXING:

Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of containers or mixing board. Mix by Volume 3 parts Base to 2 part Activator or by weight, 100 grams base to 62 grams activator. Mix throughly to produce an even colored and streak-free material. Add concrete mortor at 32 lbs. (14.5) per gallon of mixed resin. Increase or decreased amount of mortor as conditions require.

THINNING:

Never thin.

APPLICATION:

Use towel, heavy squeegee, caulking gun or putty knife. Work material into profile of substrate to achieve maximum adhesion and to remove any entrapped air. Contour to correct form with putty knife or plastic applicator. Large holes can be bridged with glass cloth or metal. Material can be shaped by sanding/grinding before full cure.

APPLICATION TEMPERATURE:

Material: Keep between 55 to 95ºF(17 to 35ºC). Substrate : Keep between 45 to 105ºF(7 to 40ºC). The difference in tem- perature of the substrate and the material should never exceed 10ºF (5ºC). Substrate shall be a minimum of 5ºF (3ºC) above dew point. Do not apply if relative humidity exceeds 90%. If nessary heat metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area overnight (75ºF to 24ºC) for easy mixing. If nessary base component of material can be heated by microwave for 30-45 seconds for a 1 KG Base unit or by warm water bath. Heat activator by warm water bath only. If nessary let material cool before application.

OVERCOAT/CURE TIME:

Recoat between 6 to 12 hours at 77ºF (35ºC). If overcoat window is exceeded abrade surface with course sandpaper, grinder or brush blast. Full cure before immersion seven days at 77ºF. Add 1 day additional cure time for each 10ºF below 77ºF. Subtract15 hours of cure time for each 10ºF above 77ºF. Force cure with heatbfor best performance: 12 hours at 120ºF(49ºC). Do not use gas or kerosene heaters.

 

CLEAN UP: Clean up tools immediatly after use with M.E.K. or similar

 

WARNING: Base contains epoxy resin. Activator contains alkaline amines, a strong sensitizer. May cause skin irritation, sensitization or other allergic responses. Use with good ventilation, particularly if heated or sprayed. Prevent all contact with skin or eyes. Wear protective clothing, goggles, gloves or barrier creams. Keep containers closed when not in use. Wash thoroughly after handling. In case of skin contact immediately wash with soap and water. In case of eye contact, flush with water for 15 minutes. If irritation persists seek medical attention.

Product Photos:

Related Cases:

Related Links:

Related Videos: