ARCOR EE 92
GENERIC TYPE: AMINE CURED 100% SOLIDS EPOXY REBUILDING COMPOUND
DESCRIPTION AND RECOMMENDED USES: ARCOR® EE-92 is an Epoxy Rebuild and is comparable to our EE-94 in resin and amine design but with smaller mesh Ceramic Beads. These high crush strength ceramic beads coupled with the addition of high-strength Kevlar fibers, gives EE-92 an extremely high level of impact, abrasion and compressive strengths. This self-wetting formulation can be applied without a primer, can be applied at +1/2″ (500 mils, 12.5mm) on verticals and overheads and can be levelled to a smooth finish requiring no topcoat dramatically minimizing application & turn-around time. ARCOR EE-92 is a very convenient 1 :1 Mix Ratio, by Weight or Volume, ideal for easy breakdown in-field. Similar to our 8506 in application, look and feel.
FOR INDUSTRIAL USE ONLY
TEMPERATURE:General Immersion service (chemistry dependant);
Max. 140°F (60C) (Spike to 200F, 3hrs (93C)); Dry to 325°F (163C) (Spike to 450F).
Inorganic Acids: Very Good
Organic Acids: Good
Organic Solvents: Very Good
SOLIDS BY VOLUME: 100%
FLEXURAL STRENGTH: 16,100 psi (ASTM D790/7 days)
COMPRESSIVE STRENGTH: 18,900 psi (ASTM D695/7 days)
TENSILE SHEAR: 2,590 psi (ASTM D1002/steel:steel)
APPLICATIONS:Ore & Coal Handling Equipment, Chutes, Pumps, Impellers, Propellers, Valves, HydroWheels, Pipe Elbows.
Any high wear immersion or non-immersion application especially with chemical and/or elevated temperature exposure.
POT LIFE: 23 Min/KG @ 75ºF
MIX RATIO: 1:1 by volume (Base:Activator) 100 gm: 100 gm by weight
SHELF LIFE: 5 years at 55-95ºF, 13-35ºC
COVERAGE: Varies with thickness applied
WEIGHT PER GALLON: 15.1 lbs (6.9 KG)
To place orders and/or obtain pricing information contact:
Novolac Epoxy Technologies Inc.
PO Box 990
Harwich, MA 02645
Email: [email protected] ; Tel: 508.385.5598
Manufacturer makes no warranty either expressed or implied including warranties of merchant ability or fitness for a particular purpose for this product. Under no circumstances will the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability, or any other theory arising out of use of this product.
SEE MATERIAL SAFETY DATA SHEET BEFORE HANDLING THIS PRODUCT
Metal surfaces are to be cleaned and degreased then abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-6 Commercial Finish minimum 4 mil profile. Immersion applications to SSPC SP-10 Near White metal, 4 to 6 mil profile. Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted surfaces to be rebuilt as quickly as possible to prevent oxidation of the surface and allow time for proper rebuilding of the damaged area. Ca be used to rebuild damaged concrete. Concrete should be degreased, neutralized, and dry.
Thoroughly mix Activator into Base with mixing stick scraping sides and bottom of container or mixing board. Mix by volume 1 parts Base to 1 part Activator. Or by weight 1 parts Base to 1 part Activator (100: 100). Mix thoroughly to produce and even colored , streak-free material.
Use heavy plastic squeegee or putty knife. Work material into profile of substrate to achieve maximum adhesive and to remove any entrapped air. Contour to correct form with putty knife or plastic applicator. If mold or form is used be sure to coat its surface with a release agent to prevent adhesion of the material. Machining is possible using diamond tipped tools only. Grinding is possible only if done within 2 hours of application at 77°F (add 1 hour for each 10°F below 77°F, subtract 1 /2 hour for each 10°F above 77°F).
Material: keep between 55 and 95°F (17-35°C). Substrate: keep between 45-105°F (7-40°C). The difference in temperature of the substrate and the material should never exceed 10°F, 5°C. Substrate shall be a minimum of 5°F (3°C) above dew point. Do not apply if relative humidity exceeds 90%. If necessary heat the metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area overnight (75°F+) for ease of mixing. If necessary Base component of material can be heated by microwave for 30 seconds for a 1 KG Base unit or by warm water bath. Heat Activator by warm water bath only. If necessary let material cool before application.
Recoat as soon as possible while material is still soft, within 2-4 hours at 77°F. 25°C. Max overcoat is 12 hours at 77F(25C). If overcoat window is exceeded abrade surface with course sandpaper, grinder or brush blast. Full cure before immersion 36 hours at 77°F. Force Cure with heat for best performance for 1 hour at 200°F, 93°C, 12 hours at 120°F, 49°C.
CLEAN UP: Clean tools immediately after use with Acetone or MethylEthylKetone (M.E.K.). Use 98%+ lsopropyl Alcohol in solvent controlled environments.
WARNING: Base contains epoxy resin. Activator contains alkaline amines, a strong sensitizer. May cause skin irritation, sensitization or other allergic responses. Use with good ventilation, particularly if heated or sprayed. Prevent all contact with skin or eyes. Wear protective clothing, goggles, gloves or barrier creams. Keep containers closed when not in use. Wash thoroughly after handling. In case of skin contact immediately wash with soap and water. In case of eye contact, flush with water for 15 minutes. If irritation persists seek medical attention.