ARCOR S 20
GENERIC TYPE: AMINE CURED 100% SOLIDS EPOXY NOVOLAC TOPCOAT
DESCRIPTION AND RECOMMENDED USES: ARCOR® S-20 is a solvent free, high functionality epoxy Novolac designed particularly as a protective coating for metals in highly aggressive environments especially high chemical, high abrasion and elevated temperatures. The ARCOR® S-20 multi functional chemistry produces an excellent coating suited for aggressive acid and caustic service, ethanol. butanol, organic solvents. ARCOR® S-20 can be applied up to 30 mils by hand without slump. Ideal for single coat spray application at 15 mils up to 45 mils pinhole free. Ambient cure. Ready for service within 24 hours. Easily repaired in-field. Ideal for wide array of chemicals and rapid turn-around for Chemical barges,Tanker Trucks & Portable Acids Tanks.
FOR INDUSTRIAL USE ONLY
TEMPERATURE: Immersion service
Max.235ºF (113ºC); Spike to 375ºF (190ºC) (3 Hrs)
Dry 375ºF (190ºC); Spike to 475ºF (246ºC) (3 Hrs)
Inorganic Acids: Excellent
Organic Acids: Excellent
Organic Solvents: Excellent
FLEXIBILITY: Good. Very Good with Polyester or
Fiberglass Mat; 1.5 oz/ft2 (.5 KG/M2)
FILM THICKNESS: Hand application 15-30 mils/
Spray Application 15-45 mills/coat(.375-1.125mm)
APPLICATIONS: Chemical Barge Tanks, Chemical
Tanker Trucks, Neutralization Tanks, Caustic
Tanks,Clarifiers, Demin Tanks, Chemical Drain
Troughs, Secondary Containment, Pumps. FGD;
SOLIDS BY VOLUME: 100%
VISCOSITY: 65,000-85,000 cps
POT LIFE: 20 MIN/Gal @ 72ºF COLOR: Blue, Gray.
MIX RATIO: 2:1 by Volume (Base:Activator) 2:1 by weight
SHELF LIFE: 5 Years at 55-95ºF (13-35ºC) COVERAGE: @ 20 mils: 80 sf/gal (add 20% waste)
WEIGHT PER GALLON: 12.6 lbs (5.7 KG)
To place orders and/or obtain pricing information contact:
ARCOR Epoxy Inc. PO Box 273
South Dennis, MA 02660
Manufacturer makes no warranty either expressed or implied including warranties of merchantability or fitness for a particular purpose for this product. Under no circumstances will the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability, or any other theory arising out of use of this product.
SEE SDS (SAFETY DATA SHEET) BEFORE HANDLING THIS PRODUCT
Steel surfaces are to be abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-10 Near White metal finish. Immersion applications to SSPC SP-5 White metal with 4-5 mil profile. Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted surfaces to be primed with ARCOR® S-20, EE-11 Prime depending upon substrate and Concrete surfaces : Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pressure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR® S-20 , EE-11 Prime, EE-79, EE-10 depending upon substrate and service.
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade. Mix by Volume 2 parts Base to 1 part Activator. Or by weight 2 parts Base to 1 part Activator.
Brush: medium to stiff bristle of sufficient quality that bristles do not pull out and stick in coating (epoxy glued bristles are best). Trim or tape to <1” nap.
Roller: use good quality 1/4” – 3/8” nap.
Plural Spray: .029-.039 RAC tip, 2,500 – 3,500 PSI, Heat to 160ºF Base, 110ºF Activator.
Airless Spray use .033-.041 RAC tip, 4,500-5,500 PSI(65:1+). Heat Base to 85F and Act to 75F minimum.
(Caution: Short Pot-Life)
Conventional Spray: Not Recommended
All spray equipment should employ traps to prevent water and oil from contaminating coating and 30 mesh screens prevent particulate contamination. Use Spray Gun such as Graco XTR-7.
Material: Keep between 55 to 95ºF (13 to 35ºC). Substrate : Keep between 45 to 105ºF (7 to 40ºC). The difference in temperature of the substrate and the coating should never exceed 10ºF (5ºC). Substrate shall be a minimum of 5º(3ºC) above dew point. Do not apply if relative humidity exceeds 80%. If necessary heat metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area over night(75ºF+, 24ºC) for ease of mixing. If necessary base component of material can be heated by microwave for 30 seconds for a 1 KG Base unit or by warm water bath Heat activator by warm water bath only. If necessary let material cool before application.
OVERCOAT / CURE TIME:
By Brush or Roller re-coat between 3 and 12 hours at 72ºF (25ºC). When spraying a single coat is best at 15-45 mils depending on service. If doing multiple spray coats, re-coat between 2 and 12 hours. Full cure before immersion 24 Hours at 72ºF. Without de-humidification keep re-coat times as short as possible or wipe with Acetone immediately prior to re-coat especially if humidity exceeds 60%.
CLEAN UP: M.E.K., Acetone or other Ketone blend. For solvent controlled areas use isopropyl alcohol.
WARNING: Base contains epoxy resin. Activator contains alkaline amines, a strong sensitizer. May cause skin irritation, sensitization or other allergic responses. Use with good ventilation, particularly if heated or sprayed. Prevent all contact with skin or eyes. Wear protective clothing, goggles, gloves or barrier creams. Keep containers closed when not in use. Wash thoroughly after handling. In case of skin contact immediately wash with soap and water. In case of eye contact, flush with water for 15 minutes. If irritation persists seek medical attention.