Updated May 2020
GENERIC TYPE: AMINE CURED 100% SOLIDS EPOXY PRIMER, TOPCOAT
DESCRIPTION AND RECOMMENDED USES: ARCOR™ EE-70 is a solvent free, moisture insensitive epoxy coating suitable for immersion and non-immersion service. ARCOR™ EE-70 produces a tough, chemical and abrasion- resistant coating on ferrous and non-ferrous metals, concrete (damp or dry) or wood.Certified by National Sanitation Foundation(NSF), Standard 61 for Potable Water, and USDA for Incidental Food Contact. Excellent for application to damp or wet substrates.
FOR INDUSTRIAL USE ONLY
TEMPERATURE: Immersion service
Max.130ºF (49ºC); Spike to 160ºF (3 Hrs)
FILM THICKNESS: 10-15 mils (.26-.40 mm) Exterior: 1-2 coats, Immersion: 2-3 coats
FLEXIBILITY: Good Excellent with Fiberglass Mat; 1.5 oz/ft2 (.5 KG/M2)
APPLICATIONS: Tanks, Pipe, Flooring,
Acid/Caustic Splash Zones, Potable Water, Incidental Food Contact Areas, Wastewater Tanks,
Sewer Pipe, Petrochemical Tanks, Structural Steel.
SOLIDS BY VOLUME: 100%
VISCOSITY: 10,000-12,000 cps
POT LIFE: 35 MIN @ 72ºF
Mix Ratio: 2:1 by volume (Base:Activator) 100 gm: 67.5 gm by weight
COLOR: Blue,White (special order colors available)
SHELF LIFE: 5 Years at 55-95ºF (13-35ºC)
COVERAGE: 20-80 ft2 (1.9-7.5 M2)/gal
WEIGHT PER GALLON: 9.7 lbs (4.4 KG)
SEE MATERIAL SAFETY DATA SHEET BEFORE HANDLING THIS PRODUCT
SURFACE PREPARATION: Steel surfaces are to be abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-10 Near White metal finish. Immersion applications to SSPC SP-5 White metal. Grind flat all burrs, weld seams, radius sharp edges.
Concrete surfaces : Not Recommended for hand or roller application. Apply by heated plural or airless spray only. Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pres- sure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete.
MIXING: Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade. Mix by Volume 1.3 parts Base to 1 part Activator or by Weight 100 gm Base to 67.5 gm Activator.
THINNING: Never thin.
APPLICATION: All spray equipment should employ traps to prevent water and oil from contaminating coating and screens to prevent particulate contamination.
By Brush use medium to stiff bristle of sufficient quality that bristles do not pull out and stick in coating. Trim or tape to <1” nap.
Roller use good quality 1/8” nap.
Plural Spray use .023-.032 tip, 3,000-3,500 PSI, Heat to 130ºF Base, 110ºF Activator. Airless Spray – Not Recommended
Conventional Spray – Not Recommended
APPLICATION TEMPERATURE: Material: Keep between 55 to 95ºF (13 to 35ºC). Substrate : Keep between 45 to 105ºF (7 to 40ºC). The difference in temperature of the substrate and the coating should never exceed 10ºF (5ºC).
OVERCOAT / CURE TIME: By Brush or Roller re-coat between 6 and 8 hours at 72ºF (25ºC). When spraying re-coat between 5 and 8 hours. Full cure before immersion 3 Days at 77ºF. Force Cure: 12 hours at 150ºF (66ºC).
CLEAN UP: M.E.K. or similar
WARNING: Base contains epoxy resin. Activator contains alkaline amines, a strong sensitizer. May cause skin irritation, sensitization or other allergic responses. Use with good ventilation, particularly if heated or sprayed. Prevent all contact with skin or eyes. Wear protective clothing, goggles, gloves or barrier creams. Keep containers closed when not in use. Wash thoroughly after handling. In case of skin contact immediately wash with soap and water. In case of eye contact, flush with water for 15 minutes. If irritation persists seek medical attention.
Are you interested in this product?
Want to know more?
To place orders and/or obtain pricing information contact or call our offices below:
Manufacturer makes no warranty either expressed or implied including warranties of merchantability or fitness for a particular purpose for this product. Under no circumstances will the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability, or any other theory arising out of use of this product.