GENERIC TYPE: AMINE CURED 100% SOLIDS EPOXY REBUILD

DESCRIPTION AND RECOMMENDED USES: ARCOR® EE-951 HT is a solvent free epoxy 3.6 functionality Novolac designed particularly as a rebuilding material for metals in highly aggressive chemical and temperature immersion service. It is Ideally suited for restoration or cladding material for corrosion and abrasion protection. ARCOR® EE-951 HT can be applied up to 500 mils without slump.

FOR INDUSTRIAL USE ONLY

SPECIFICATION DATA:

TEMPERATURE: Immersion service

Max 375ºF (190.5ºC);
Spike to 475ºF (246.1ºC) (3 Hrs) Recommended Force Cure at 175ºF (79.4ºC) @ 2 hrs;
300ºF (148.9ºC) @ 3 hrs; Dry to 500ºF; Spike to 580ºF(3 Hrs)

SOLIDS BY VOLUME: 100%

VISCOSITY: Putty

POT LIFE: 25 MIN / KG @ 72ºF

MIX RATIO: 3:1 by Volume (Base : Activator) 100 gm: 33 gm by Weight

COLOR:  Gray

ABRASION: Excellent

FILM THICKNESS: Good Fair Flexural Strength 12,000 psi

Flexibility: Very Good Excellent with Polyester Mat; 1.5 oz/ft² (5. KG/M²)

APPLICATIONS: Tank Linings, Ion Exchange Filters, FGD, Ducts, Mix Zones, I.D. Fans, Scrubbers, Concrete Secondary Containments

SHELF LIFE: 5 Years at 55-95ºF (13-35ºC)

COVERAGE: Varies with thickness applied

WEIGHT PER GALLON: 12.1 lbs (5.6 KG)

Manufacturer, Novolac Epoxy Technologies Inc., makes no warranty either expressed or implied including warranties of merchantability or fitness for a particular purpose for this product. Under no circumstances will the manufacturer be liable for incidental, consequential or other damages, breach of warranty, strict liability, or any other theory arising out of use of this product. The information and or recommendations contained herein are based on standard Product and are proprietary and furnished solely for the use of our customers. This information is provided in good faith and believed to be true and accurate as of the date/version of this document. As the manufacturer has no control over the use conditions or application process of the parties using this product, the manufacturer cannot accept responsibility for loss, injury or other damages resulting from the use of the Product or this or any other information provided by the manufacturer. Therefore, no guarantees of any kind, expressed or implied, are made by the manufacturer, Novolac Epoxy Technologies Inc., regarding this, or any, product manufactured by them or any contracted or licensed manufacturer. ARCOR® epoxy products do not provide structural integrity or improvement. They are only used to provide protection from corrosion, wear, abrasion and chemical attack on a given substrate and only to the extent provided for in the Data Sheets, Technical Data Sheets, Safety Data Sheets and any other information as supplied in writing directly from manufacturers technical support.

APPLICATION SHEET

REVISED 1/2015

SEE MATERIAL SAFETY DATA SHEET BEFORE HANDLING THIS PRODUCT

SURFACE PREPARATION: Steel surfaces are to be abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-10 Near White metal finish. Immersion applications to SSPC SP-5 White metal 3 to 5 mil profile. Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted ferrous surfaces to be primed immediately with ARCOR™ S-30 Prime or ARCOR™ EE- 101 to prevent oxidation of surface. Concrete surfaces should be degreased if oil and grease contamination is present.

Degreased surface shall be high pressure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR™ EE-101, EE-111.

Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pres- sure washed, acid etched and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. Prime with ARCOR™ EE-101.

MIXING: Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of container or mixing board. Mix by Volume 3 parts Base to 1 part Activator. Mix thoroughly to produce an even colored, streak-free material.

THINNING: Never thin.

APPLICATION: Use heavy plastic squeegee or putty knife. Work material into profile of substrate to achieve maximum adhesion and to remove any entrapped air. Contour to correct form with putty knife or plastic applicator. If mold or form is used, coat its surface with a release agent to prevent adhesion of the material. Machining is possible using carbide tipped tools.

Grinding is possible if done within 14 hours of application at 77ºF, 25ºC (add 1-1/2 hour for each 10ºF below 77º, subtract 1 hour for each 10º above 77ºF). Large holes and cracks can be bridged with glass or metal cloth.

APPLICATION TEMPERATURE: Material: Keep between 55 to 95ºF (17 to 35ºC). Substrate: keep between 45 to 105ºF (7 to 40ºC). the difference in temperature of the substrate and the material should never exceed 10ºF, 5ºC. Substrate shall be a minimum of 5ºF (3ºC) above dew point. Do not apply if relative humidity exceeds 90%. If necessary heat the metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area overnight (75ºF+) for ease of mixing. If necessary Base component of material can be heated by microwave for 30-45 seconds for a 1 KG Base unit or by warm water bath. Heat activated by warm water bath only. If necessary let material cool before application.

OVERCOAT / CURE TIME: Re-coat while material is still soft, between 1 to 2 hours at 77ºF, 25ºC. If overcoat window is exceeded abrade surface with course sandpaper, grinder or brush blast. Full cure before immersion 36 hours at 77ºF. Force cure with heat for best performance for 8 hours at 120ºF (49ºC); 2 hours at 250ºF (121ºC)

CLEAN UP: Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar

WARNING: Base contains epoxy resin. Activator contains alkaline amines, a strong sensitizer. May cause skin irritation, sensitization or other allergic responses. Use with good ventilation, particularly if heated or sprayed. Prevent all contact with skin or eyes. Wear protective clothing, goggles, gloves or barrier creams. Keep containers closed when not in use. Wash thoroughly after handling. In case of skin contact immediately wash with soap and water. In case of eye contact, flush with water for 15 minutes. If irritation persists seek medical attention. Consult the Product Safety Data Sheets (SDS) BEFORE USE!

The information and or recommendations contained herein are based on standard Product and are proprietary and furnished solely for the use of our customers. This information is provided in good faith and believed to be true and accurate as of the date/version of this document. As the manufacturer has no control over the use conditions or application process of the parties using this product, the manufacturer cannot accept responsibility for loss, injury or other damages resulting from the use of the Product or this or any other information provided by the manufacturer. Therefore, no guarantees of any kind, expressed or implied, are made by the manufacturer, Novolac Epoxy Technologies Inc., regarding this, or any, product manufactured by them or any contracted or licensed manufacturer.